下面列出擠出的是Xtel XE系列化合物（Xtel PPS）擠出工藝指南
•  28:1 to 32:1 L/D
•  General Purpose screw with 2.5:1 to 3:1
Compression ratio. Mixing head optional.
• 20/60/100 Screen-pack
• Rupture disk
•  Heated die clamp
Melt Pump
•  Melt pumps are beneficial for producing
the most consistent and uniform sheet,
but are not required for processing Xtel  XE Series compounds（Xtel  PPS）
Sheet Die
•  Die head suitable for low viscosity, high
temperature materials
烘干溫度
•  275°F to 300°F (135°C to 150°C)至少4個(gè)小時(shí)
•  Hopper driers and/or desiccant driers are
not required

Temperature Profile for 3:1 Screw
  Extruder Zone 1  550°F  (288°C)
  Extruder Zone 2  570°F  (300°C)
  Extruder Zone 3  570°F  (300°C)
  Extruder Zone 4  570°F  (300°C)
  Extruder Zone 5  570°F  (300°C)
  Adaptor 570°F  (300°C)
  Die 1 560°F  (293°C)
  Die 2 560°F  (293°C)
  Die 3 560°F  (293°C)
*Lowering the temperatures after startup may
help with finish quality.
Roll Stack Temperature Profile
Roll #1    260°F  (126°C)
Roll #2    275°F  (135°C)
Roll #3    290°F  (143°C)

加工注意事項(xiàng)：
Xtel PPS需要足夠的加熱時(shí)間,啟動擠出機(jī)至關(guān)重要的是確保穩(wěn)定加工的溫度,。如果溫度不夠擠出將造成的阻塞。 Xtel  XE系列化合物（Xtel PPS）過程更擠出率較高的地方是從螺桿融化而不是加熱器,。擠出機(jī)應(yīng)調(diào)整到高于50％的過程中運(yùn)行的溫度,，同時(shí)盡量減少停留時(shí)間。皂泡,，煙霧或凝膠都是在擠出機(jī)里過于熱,，時(shí)間太久而造成的。溫度適當(dāng)調(diào)整,，但模具不低于540華氏度（282℃）設(shè)置。如果需要熔體溫度降低,，選的調(diào)整擠出機(jī)的溫度分布，而不是降低模具溫度,。持續(xù)融化以上600 °F對于長期的時(shí)間段（315℃）的溫度會導(dǎo)致材料熱降解的結(jié)果,。

 
清洗程序：加工設(shè)備Xtel  XE版系列化合物（Xtel PPS）的傳輸速率較佳處理用分?jǐn)?shù)熔體流動高密度聚乙烯（Marlex HHM 50100）來清洗,。料桶和螺釘應(yīng)該清洗潔凈,。

 如有疑問可繼續(xù)瀏覽更多Xtel PPS加工指南或聯(lián)絡(luò)我公司客戶服務(wù)中心索取該資料.